Product Description
Designed for the manufacture of lightweight, high-performance composites, Pro-Set INF-117G biosourced epoxy infusion resin is a solution resistant to long-term cyclic loads and extreme conditions. Thanks to its low viscosity, it guarantees exceptional impregnation and adhesion. For even better performance, INF-117G can be post-cured.
Packaging Options
- Resin packaging: available in 5kg and 25kg.
- Bio-sourced hardeners: medium cure (2048) and slow cure (2049)
- Hardener packaging: available in 1.7kg and 2x 4.25kg
Technical Properties
INF-117G / INF-2048 (Room temperature x 1 week)
| Mixing ratio by weight | 2.94:1 (Resin:Hardener) |
| Mixing ratio by volume | 2.56:1 (Resin:Hardener) |
| Hardness (Type D) | 83 |
| Mixed viscosity 25°C | 440 mPas |
| Compressive strength | 94.1 MPa |
| Tensile strength | 64.8 MPa |
| Tensile elongation | 2.8% |
| Flexural strength | 99.5 MPa |
| Ultimate Tg by DMA | 65°C |
| Ultimate Tg by DSC | 69.6°C |
INF-117G / INF-2049 (Ambient temperature x 24H + 50°C x 16H)
| Mixing ratio by weight | 2.94:1 (Resin:Hardener) |
| Mixing ratio by volume | 2.44:1 (Resin:Hardener) |
| Hardness (Type D) | 82 |
| Mixed viscosity 25°C | 220 mPas |
| Compressive strength | 86.8 MPa |
| Tensile strength | 58.4 MPa |
| Tensile elongation | 4.5% |
| Flexural strength | 96 MPa |
| (Gelling at TA + 50°C x 16H) | |
| Ultimate Tg by DMA | 65°C |
| Ultimate Tg by DSC | 69.6°C |
Additional Information
For further information, please consult the product data sheet.