Product Overview
Specializing in the production of strong, lightweight composites, INF-117G biobased infusion epoxy resin, together with its different hardeners: INF-2048 (Medium Hardener) and INF-2049 (Slow Hardener), stands up to harsh environments and repetitive stresses over the long term. With very low viscosity, it ensures superior adhesion and penetration. The performance of this resin can be optimized through a post-curing process.
Packaging Information
- Resin packaging: available in 5kg and 25kg
- Bio-sourced hardeners: medium cure (2048) and slow cure (2049)
- Hardener packaging: available in 1.7kg and 8.5kg
Technical Properties
INF-117G / INF-2048 (Room temperature x 1 week)
| Mixing ratio by weight |
2.94:1 (Resin:Hardener) |
| Mixing ratio by volume |
2.56:1 (Resin:Hardener) |
| Hardness (Type D) |
83 |
| Mixed viscosity 25°C |
440 mPas |
| Compressive strength |
94.1 MPa |
| Tensile strength |
64.8 MPa |
| Tensile elongation |
2.8% |
| Flexural strength |
99.5 MPa |
| Ultimate Tg by DMA |
65°C |
| Ultimate Tg by DSC |
69.6°C |
INF-117G / INF-2049 (Ambient temperature x 24H + 50°C x 16H)
| Mixing ratio by weight |
2.94:1 (Resin:Hardener) |
| Mixing ratio by volume |
2.44:1 (Resin:Hardener) |
| Hardness (Type D) |
82 |
| Mixed viscosity 25°C |
220 mPas |
| Compressive strength |
86.8 MPa |
| Tensile strength |
58.4 MPa |
| Tensile elongation |
4.5% |
| Flexural strength |
96 MPa |
(Gelling at TA + 50°C x 16H)
| Ultimate Tg by DMA |
65°C |
| Ultimate Tg by DSC |
69.6°C |
Additional Information
For further details, please consult the product data sheet.