The Seacoat Pro Two-Component Epoxy Primer by JET BLACK is a premium anticorrosion primer designed for marine environments, suitable for application above and below the waterline. This high-performance primer is formulated to reinforce and protect wood, metal, and polyester surfaces, ensuring optimal adhesion for subsequent antifouling or paint applications.
- Anticorrosion Protection: Provides a robust shield against corrosion, enhancing the durability of marine vessels.
- Exceptional Adhesion: Offers strong adhesion on various substrates, including polyester, steel, wood, aluminum, galvanized surfaces, and concrete.
- Impact Resistance: Increases resistance to impacts and abrasions, reducing the risk of osmosis.
- Waterproofing: Creates a waterproof layer between the hull and antifouling, significantly decreasing the likelihood of osmosis.
- Versatility: Suitable as a primer for high-traffic deck areas before applying two-component paints and as a base before applying antifouling.
- Ease of Application: Designed for easy mixing, application, and cleaning.
Technical Specifications:
- Composition: Epoxy resin, hardener, pigments, and additives.
- Coverage: Approximately 8 m² per liter per coat.
- Drying Time: Dust-free: 1 hour; Touch dry: 4 hours; Recoatable: 24 hours.
- Number of Coats: 2 to 3 coats, depending on the condition of the substrate.
- Application Equipment: Brush, roller, or spray gun.
- Mixing Ratio: 15 parts hardener to 4 parts base by volume; 15% hardener by weight.
- Application Temperature: Between 10°C and 30°C.
- Theoretical Coverage: 0.17 L/m² per coat.
- Recoatable: Can be recoated by itself.
- Pot Life: 4 to 5 hours.
Materials:
- Base Component: 590 ml of epoxy resin.
- Hardener Component: 160 ml of hardener.
Dimensions:
- Container Size: 750 ml total (590 ml base + 160 ml hardener).
Compatibility Information: The Seacoat Pro Two-Component Epoxy Primer is compatible with various substrates, including composite materials, gelcoat, aluminum and its alloys, plywood, steel, cast iron, galvanized sheet metal, and electro-galvanized surfaces, provided they are properly prepared.